Atom Arc 8018-SR
Atom Arc 8018-SR is an all-position low hydrogen electrode. The moisture resistance and welder appeal is similar to other Atom Arc electrodes. Atom Arc 8018-SR was developed to maintain 80 ksi (552 MPa) after 50 hours stress relieving.
Industries
- Power Generation
Welding Process
- SMAW/MMA (Stick)
Typical Charpy V-Notch Properties
stress relieved | ||||
8 hr | ||||
20 hr | ||||
50 hr | ||||
8 hr | ||||
20 hr | ||||
50 hr |
Typical Tensile Properties
Condition | Stress Relieved | Stress Relieved | Stress Relieved |
Reduction in Area | 75 % | 78 % | 76 % |
Tensile Strength | 587 MPa (85 ksi) | 562 MPa (82 ksi) | 580 MPa (85 ksi) |
Yield Strength | 490 MPa (71 ksi) | 470 MPa (69 ksi) | 495 MPa (72 ksi) |
Elongation | 29 % | 32 % | 30 % |
Testing Time | 8 hr | 50 hr | 20 hr |
Testing Temperature | 621 degC (1150 degF) | 621 degC (1150 degF) | 621 degC (1150 degF) |
Deposition Data
Current | Deposition Rate | Diameter | Deposition Efficiency (%) | Optimal Amps |
130-220 A | 1.7 kg/h (3.8 lb/h) | 4.0 mm (5/32 in.) | 73.5 % | 170 A |
90-160 A | 1.2 kg/h (2.6 lb/h) | 3.2 mm (1/8 in.) | 71.6 % | 120 A |
200-300 A | 2.4 kg/h (5.4 lb/h) | 4.8 mm (3/16 in.) | 74.6 % | 250 A |
200-300 A | 2.2 kg/h (4.9 lb/h) | 4.8 mm (3/16 in.) | 76.4 % | 200 A |
70-100 A | 0.8 kg/h (1.7 lb/h) | 2.4 mm (3/32 in.) | 66.3 % | 90 A |
90-160 A | 1.2 kg/h (2.7 lb/h) | 3.2 mm (1/8 in.) | 70.9 % | 140 A |
130-220 A | 1.1 kg/h (3.1 lb/h) | 4.0 mm (5/32 in.) | 75 % | 140 A |
Classifications
Classifications |
ASME SFA 5.5 : AWS A5.5 : E8018-G H4R |
Consumable Characteristics
Coating Type | Low-hydrogen iron powder |
0 | |
Welding Current | AC or DC+ |
Typical Weld Metal Analysis %
Typical Weld Metal Analysis % | ||||||||||||||
C | Cr | Cu | Mn | Mo | Nb | Ni | P | Si | V | |||||
0.075 % | 0.10 % | 0.114 % | 1.12 % | 0.26 % | 0.003 % | 0.90 % | 0.01 % | 0.34 % | 0.009 % |