Atom Arc T
Atom Arc T was developed for welding T-1 steel in all applications. Mechanical properties of the welded joints equal or exceed the properties of the base steel in either the as welded or stress relieved condition, thus giving 100% design joint efficiency. In addition, Atom Arc T electrodes are suitable for many other applications, particularly where high-strength welds with excellent low temperature impact properties are required.
Industries
- Bridge Construction
- Civil Construction
- Industrial and General Fabrication
- Mobile Equipment
- Railcars
- Ship/Barge Building
Welding Process
- SMAW/MMA (Stick)
Typical Charpy V-Notch Properties
| as welded | ||||
| stress relieved | ||||
| 1 hr | ||||
| 1 hr | ||||
| 1 hr | ||||
Typical Tensile Properties
| Condition | As Welded | Stress Relieved |
| Flat Position | ||
| Reduction in Area | 62 % | 63 % |
| Tensile Strength | 795 MPa (115 ksi) | 770 MPa (112 ksi) |
| Yield Strength | 725 MPa (105 ksi) | 705 MPa (102 ksi) |
| Elongation | 23 % | 23 % |
| Testing Time | 1 hr | |
| Testing Temperature | 552 degC (1025 degF) |
Deposition Data
| Current | Deposition Rate | Diameter | Deposition Efficiency (%) | Optimal Amps |
| 70-100 A | 0.8 kg/h (1.7 lb/h) | 2.4 mm (3/32 in.) | 66.3 % | 90 A |
| 90-160 A | 1.2 kg/h (2.6 lb/h) | 3.2 mm (1/8 in.) | 71.6 % | 120 A |
| 90-160 A | 1.2 kg/h (2.7 lb/h) | 3.2 mm (1/8 in.) | 70.9 % | 140 A |
| 130-220 A | 1.1 kg/h (3.1 lb/h) | 4.0 mm (5/32 in.) | 75 % | 140 A |
| 130-220 A | 1.7 kg/h (3.8 lb/h) | 4.0 mm (5/32 in.) | 73.5 % | 170 A |
| 200-300 A | 2.2 kg/h (4.9 lb/h) | 4.8 mm (3/16 in.) | 76.4 % | 200 A |
| 200-300 A | 2.4 kg/h (5.4 lb/h) | 4.8 mm (3/16 in.) | 74.6 % | 250 A |
| 250-350 A | 2.9 kg/h (6.5 lb/h) | 5.6 mm (7/32 in.) | 75 % | 250 A |
| 250-350 A | 3.3 kg/h (7.2 lb/h) | 5.6 mm (7/32 in.) | 74 % | 300 A |
Classifications
| Classifications |
ASME SFA 5.5 : AWS A5.5 : E11018M H4R |
Approvals
| Approvals |
ABS AWS A5.5: E11018-M CWB CSA W48 E7618-M-H4 QPL-22200/1 MIL-11018-M |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Coating Type | Low-hydrogen iron powder |
| 0 | |
| Welding Current | AC or DC+ |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Cr | Cu | Mn | Mo | Nb | Ni | P | S | Si | V | ||||
| 0.048 % | 0.23 % | 0.072 % | 1.46 % | 0.35 % | 0.004 % | 1.83 % | 0.01 % | 0.01 % | 0.28 % | 0.010 % | ||||