Dual Shield II 4130 SR
Dual Shield II 4130 SR is an all position flux cored wire for welding low alloy, high strength steels such as 4130. Ideal for offshore oil and gas topsides and platforms requiring high corrosion resistance with stress relieved high strength and low temperature impact toughness properties. Excellent welder appeal and mechanical properties after PWHT. Meets ANSI/NACE MR0175/ISO 15156-1. Typical Diffusible Hydrogen: <4 ml/100g of deposited metal.
Industries
- Offshore Oil
Welding Process
- FCAW (Flux Core)
Typical Charpy V-Notch Properties
as welded | ||||
stress relieved 6g pipe | ||||
2 hr | ||||
stress relieved vertical postition | ||||
2 hr |
Typical Tensile Properties
Condition | Elongation | Tensile Strength | Testing Temperature | Testing Time | Yield Strength |
Stress Relieved | 26 % | 731 MPa (106 ksi) | 620 degC (1150 degF) | 2 hr | 648 MPa (94 ksi) |
Recommended Welding Parameters
Current | TTW Dist. | Voltage | Wire Diameter | Wire Feed Speed |
150-170 A | 19 mm (3/4 in.) | 23-24 V | 1.2 mm (.045 in.) | 432 cm/min (170 in./min) |
180-220 A | 16 mm (5/8 in.) | 24-26 V | 1.2 mm (.045 in.) | 719 cm/min (283 in./min) |
230-280 A | 16 mm (5/8 in.) | 26-28 V | 1.2 mm (.045 in.) | 1016 cm/min (400 in./min) |
Deposition Data
Current | Diameter | TTW Dist. | Voltage | Wire Feed Speed |
150-170 A | 1.2 mm (.045 in.) | 19 mm (3/4 in.) | 23-24 V | 4,32 m/min (170 in./min) |
180-220 A | 1.2 mm (.045 in.) | 16 mm (5/8 in.) | 24-26 V | 7,19 m/min (283 in./min) |
230-280 A | 1.2 mm (.045 in.) | 16 mm (5/8 in.) | 26-28 V | 10,16 m/min (400 in./min) |
Classifications
Classifications |
AWS A5.29/A5.29M, ASME SFA 5.29 : E101T1-GM AWS A5.36/A5.36M : E101T1-M21AP5-G-H4 |
Typical Weld Metal Analysis %
Typical Weld Metal Analysis % | ||||||||||||||
C | Cr | Mn | Mo | Ni | P | S | Si | |||||||
0.05 % | 0.03 % | 2.0 % | 0.43 % | 0.90 % | 0.011 % | 0.006 % | 0.3 % |