Stoody Brilliant 2209 T-1 AP

The following items have been added to your list


x

Brilliant 2209 T-1 AP is designed for all position welding of duplex stainless steels which contain approximately 22% chromium. The composition is balanced to achieve a microstructure of approximately 50% ferrite and 50% austenite in the weld deposit. The alloy exhibits a spray-like arc transfer, easy slag removal, and can be welded within a wide range of parameters. AWS classification A5.22 E2209T1-X.

BUY NOW


Features

  • All position weldability
  • Spray-like arc transfer
  • AWS Classification A5.22 E22091T1-X


Typical Charpy V-Notch Properties

As Welded
Impact Value 44 ft-lb
Impact Value 60 J
As Welded Testing Temperature -40 °C
As Welded Testing Temperature -40 °F

Typical Tensile Properties

ElongationShielding GasTensile Strength Yield Strength
27.5 %100% CO2786 MPa (114 ksi)607 MPa (88 ksi)

Deposition Data

Current Deposition Type Diameter TTW Dist. Voltage Wire Feed Speed
75% Ar - 25% CO2
130-220 A Full Range 1.2 mm (.045 in.) 13 mm (1/2 in.) 24-27 V 856-1435 cm/min (227-565 in./min)
170-300 A Full Range 1.6 mm (1/16 in.) 13 mm (1/2 in.) 25-28 V 394-813 cm/min (155-320 in./min)

Classifications

Grade E2209T1-X
Name AWS A5.22

Typical Weld Metal Analysis %

C Cr Fe Mn Mo N Ni Si
0.38 % 22.3 % BAL % 1.2 % 3.2 % 0.10 % 9.6 % 0.5 %