Coreshield 8

Typical Charpy V-Notch Properties

as welded

Typical Tensile Properties

Condition	Elongation	Tensile Strength	Yield Strength
As Welded	24 %	565 MPa (82 ksi)	465 MPa (67 ksi)

Deposition Data

Current	Deposition Rate	Diameter	Deposition Efficiency (%)	Wire Feed Speed
200 A	2.8 kg/h (6.13 lb/h)	1.8 mm (0.072 in.)	79.4 %	406 cm/min (160 in./min)
225 A	3.3 kg/h (7.32 lb/h)	1.8 mm (0.072 in.)	80.3 %	483 cm/min (190 in./min)
155 A	1.9 kg/h (4.16 lb/h)	1.6 mm (1/16 in.)	78.6 %	381 cm/min (150 in./min)
180 A	2.3 kg/h (5.14 lb/h)	1.6 mm (1/16 in.)	79.6 %	470 cm/min (185 in./min)
205 A	3.0 kg/h (6.60 lb/h)	1.6 mm (1/16 in.)	78.2 %	610 cm/min (240 in./min)
220 A	3.4 kg/h (7.53 lb/h)	1.6 mm (1/16 in.)	78.9 %	698 cm/min (275 in./min)
150 A	1.8 kg/h (3.96 lb/h)	2.0 mm (5/64 in.)	80.6 %	229 cm/min (90 in./min)
175 A	2.2 kg/h (4.83 lb/h)	2.0 mm (5/64 in.)	80.9 %	279 cm/min (110 in./min)
200 A	2.7 kg/h (5.93 lb/h)	2.0 mm (5/64 in.)	80.4 %	343 cm/min (135 in./min)

Classifications

Classifications

ASME SFA 5.36 : ASME SFA 5.20 : AWS A5.36 : E71T8-A2-CS3-H8 AWS A5.20 : E71T-8 JD-H8

Approvals

Approvals

ABS BV CWB CSA W48 E491T-8-H8 DB DNV-GL LR Seismic Certified "D"

Approvals are based on factory location. Please contact ESAB for more information.

Consumable Characteristics

Alloy Type	C Mn
Shielding Gas	None
Welding Current	DC-

Typical Weld Metal Analysis %

Typical Weld Metal Analysis %
Al	C	Mn	P	S	Si
0.51 %	0.19 %	0.44 %	0.010 %	0.003 %	0.15 %