Exaton 317/317L T1
FCAW wire for 18%Cr - 12%Ni – 3% Mo- N stainless steel For all-position welding. Recommended for welding type 317 stainless steel to give a maximum of 0.04% carbon in the weld deposit. The higher molybdenum content, as compared to type 316L, further reduces susceptibility to pitting corrosion. Used in the pulp and paper industry and in other severe corrosion applications involving sulfuric and sulfurous acids and their salts.
Typical Charpy V-Notch Properties
| as welded c1 shielding gas | ||||
Typical Tensile Properties
| Condition | As Welded | As Welded |
| Shielding Gas | M21 Shielding gas | C1 Shielding Gas |
| Tensile Strength | 620 MPa (90 ksi) | 600 MPa (87 ksi) |
| Yield Strength | 480 MPa (70 ksi) | 460 MPa (67 ksi) |
| Elongation | 35 % | 34 % |
Classifications
| Weld Metal |
SFA/AWS A5.22 : E317LT1-1(4) JIS Z 3323 : YF317LC KS D 3612 : YF317LC |
Consumable Characteristics
| Alloy Type | C Cr Ni Mo |
| Shielding Gas | M21, C1 (EN ISO 14175) |
| Welding Current | DC+ |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Cr | Mn | Mo | Ni | P | S | Si | |||||||
| C1 Shielding Gas | ||||||||||||||
| - | 18.4 % | - | 3.40 % | - | 0.021 % | 0.009 % | - | |||||||
| C1 Shielding gas | ||||||||||||||
| - | - | - | - | 12.5 % | - | - | - | |||||||
| C1 shielding Gas | ||||||||||||||
| 0.032 % | - | - | - | - | - | - | - | |||||||
| C1 shielding gas | ||||||||||||||
| - | - | 1.20 % | - | - | - | - | 0.80 % | |||||||
| M21 Shielding Gas | ||||||||||||||
| - | - | 1.20 % | - | 13.0 % | - | - | - | |||||||
| M21 Shielding gas | ||||||||||||||
| 0.032 % | 19.50 % | - | 3.50 % | - | 0.021 % | 0.009 % | - | |||||||
| M21 shielding gas | ||||||||||||||
| - | - | - | - | - | - | - | 0.85 % | |||||||