Exaton 309/309L HF
309/309L HF welding wire is used for MIG/MAG welding. It is particularly suitable for overlay welding and joining dissimilar steels, for example austenitic stainless steels to low alloyed or non alloyed steels. It has excellent resistance to hot cracking due to its enhanced ferrite content.
Typical Charpy V-Notch Properties
| as welded | ||||
Typical Tensile Properties
| Condition | Elongation | Tensile Strength | Yield Strength |
| As Welded | 30 % | 610 MPa (88 ksi) | 450 MPa (65 ksi) |
Recommended Welding Parameters
| Current | 150-260 A |
| Voltage | 24-29 V |
| Wire Diameter | 0.047 in. |
| Wire Diameter | 1.2 mm |
| Wire Feed Speed | 118-394 in./min |
| Wire Feed Speed | 3.0-10.0 m/min |
Classifications
| Wire Electrode |
EN ISO 14343-A : G 23 12 L SFA/AWS A5.9 : ER309L |
Approvals
| Approvals |
CE EN 13479 VdTÜV 02103 |
| Approvals are based on factory location. Please contact ESAB for more information. |
Consumable Characteristics
| Alloy Type | Austenitic (with approx. 14 % ferrite) 24 % Cr - 13 % Ni - Low C |
| Shielding Gas | M12, M13 (EN ISO 14175) |
Typical Weld Metal Analysis %
| Typical Wire Composition % | |||||||||||||||
| C | Co | Cr | Cu | FN WRC | FN deLong | Mn | Mo | N | Nb | Ni | P | S | Si | Ti | V |
| 0.01 % | 0.03 % | 23.5 % | 0.03 % | 13 % | 14 % | 1.8 % | 0.04 % | 0.05 % | 0.03 % | 13.4 % | 0.011 % | 0.001 % | 0.4 % | 0.004 % | 0.05 % |
| Typical Weld Metal Analysis % | |||||||||||||||
| 0.02 % | 0.03 % | 23.6 % | 0.01 % | 11 % | 12 % | 1.7 % | 0.02 % | 0.07 % | 0.01 % | 13.4 % | 0.013 % | 0.001 % | 0.3 % | - | 0.03 % |
Part Numbers and Accessories
ESAB EQUIPMENT WARRANTIES ARE VALID ONLY WHEN PURCHASED THROUGH AN ESAB AUTHORIZED DEALERSHIP.